Basalt fiber and nanoclay compositions, articles incorporating the same, and methods of insulating a rocket motor with the same

ABSTRACT

An insulation composition that comprises at least one nitrile butadiene rubber, basalt fibers, and nanoclay is disclosed. Further disclosed is an insulation composition that comprises polybenzimidazole fibers, basalt fibers, and nanoclay. The basalt fibers may be present in the insulation compositions in a range of from approximately 1% by weight to approximately 6% by weight of the total weight of the insulation composition. The nanoclay may be present in the insulation compositions in a range of from approximately 5% by weight to approximately 10% by weight of the total weight of the insulation composition. Rocket motors including the insulation compositions and methods of insulating a rocket motor are also disclosed.

STATEMENT REGARDING FEDERALLY SPONSORED RESEARCH OR DEVELOPMENT

The U.S. Government has a paid-up license in this invention and theright in limited circumstances to require the patent owner to licenseothers on reasonable terms as provided for by the terms of Contract No.NAS8-97238 awarded by the National Aeronautics and Space Administration(“NASA”).

FIELD OF THE INVENTION

The present invention relates to thermal insulation for use in anarticle or apparatus, such as a rocket motor. More specifically, thepresent invention relates to thermal insulation that includes a nitrilebutadiene rubber, basalt fibers, and nanoclay, as well as insulationthat includes polybenzimidazole fibers, basalt fibers, and nanoclay.

BACKGROUND OF THE INVENTION

Combustion of a propellant in a rocket motor creates a hostileenvironment that is characterized by extremely high temperatures,pressures, and turbulence. Combustion temperatures within the rocketmotor typically exceed 5000° F. (2760° C.) and pressures frequentlyexceed 1500 pounds per square inch (“psi”) (10.3 MPascal). In addition,velocities of gases produced during the combustion reach or exceed Mach0.2 near the throat of the rocket motor. To protect the rocket motor asthe propellant is combusted, heat-sensitive components of the rocketmotor are insulated. Without insulation, the combustion gases woulderode and burn through the heat sensitive components, causing the rocketmotor to fail.

The rocket motor is typically insulated with a material that providesresistance to high temperatures, pressures, and erosive flow conditions.Various insulative materials have been used, such as phenolic resins,epoxy resins, high temperature melamine-formaldehyde coatings, ceramics,or polyester resins. However, these materials, when cured, become rigidand are essentially unworkable, which makes construction of the rocketmotor and processing of these materials difficult. In addition,structures formed from these materials crack or blister when exposed tothe rapid temperature and pressure changes that occur as the propellantis burned.

Other insulative materials include an elastomeric polymer that isreinforced with asbestos, polybenzimidazole fibers, or polyaramidfibers. These insulative materials are “ablative” in that they arepartially consumed during combustion of the propellant. While theinsulative material gradually erodes, the insulative material remains inthe rocket motor for a sufficient amount of time to protect the rocketmotor while the propellant completely combusts. In other words, theinsulative material erodes at a sufficiently slow rate that adequateprotection is provided during the operation of the rocket motor.

One insulative material that has been widely used in rocket motorsincludes asbestos and a nitrile butadiene rubber (“NBR”). For instance,an asbestos-filled nitrile butadiene rubber (“ASNBR”) composition hasbeen used in the Reusable Solid Rocket Motor (“RSRM”) space shuttleprogram. When used as an insulative material, the ASNBR compositionprovides excellent ablative characteristics and good rheological,mechanical, and electrostatic properties. However, due to environmentaland health concerns with using asbestos and the closure of asbestosmines in Canada, an asbestos-free replacement for ASNBR is activelybeing sought. To date, the most suitable replacements for the ASNBRcomposition include a 7% Kevlar®-filled ethylene propylene diene monomer(“EPDM”) material, an 11% Kevlar®-filled EPDM material, and acarbon-filled EPDM material, all of which are produced by AlliantTechsystems Inc. (Edina, Minn.).

Additional EPDM compositions have been used to insulate rocket motors.United States Patent Application Publication 2002/0018847 to Guillot andU.S. Pat. No. 6,691,505 to Harvey et al. disclose, inter alia, a rocketmotor insulation that includes carbon fibers dispersed in an EPDMmatrix. The insulation also includes polybenzoxazole fibers (“PBO”),polybenzimidazole fibers, aramid fibers, iron oxide, milled glass, talc,silica, or ceramic clay.

United States Patent Application Publication 2002/0142147 to Sogabe etal. discloses a transmission belt that includes a rubber belt body and acord, which are integrated by vulcanizing the rubber of the belt body.The belt body is formed from chloroprene rubber or a hydrogenatednitrile rubber and the cord is formed from fibers ofpoly-p-phenylene-benzobisoxazole. Poly-p-phenylene-benzobisoxazole isalso known as poly-p-phenylene-2,6-benzobisoxazole or polybenzoxazole.Therefore, as used herein “PBO” refers topoly-p-phenylene-benzobisoxazole, poly-p-phenylene-2,6-benzobisoxazole,or polybenzoxazole. U.S. Pat. No. 5,891,561 to Kinoshita et al. alsodiscloses a transmission belt having a fiber cord formed from aramidfibers or PBO fibers. The fiber cord is embedded in rubber, such as ahydrogenated nitrile rubber, a nitrile butadiene rubber, chlorophenerubber, chlorosulfonated polyethylene rubber, or alkylatedchlorosulfonated polyethylene rubber.

BRIEF SUMMARY OF THE INVENTION

The present invention, in several embodiments, relates to an insulationcomposition that comprises at least one nitrile butadiene rubber(“NBR”), basalt fibers, and a nanoclay. In one embodiment, theacrylonitrile content of the NBR ranges from approximately 26% by weight(“wt %”) to approximately 35 wt %. In a further embodiment, theacrylonitrile content of the NBR ranges from approximately 30 wt % toapproximately 35 wt %. The NBR may be a copolymer of acrylonitirle andbutadiene. The NBR may be present in the insulation composition in arange from approximately 35 wt % to approximately 56 wt % of a totalweight of the insulation composition. The basalt fibers may be presentin a range of from approximately 1 wt % to approximately 6 wt % of thetotal weight of the insulation composition. Nanoclay may be present in arange of from approximately 5 wt % to approximately 10 wt % of the totalweight of the insulation composition. The insulation composition mayfurther comprise one or more additives, such as at least one reinforcingagent, at least one tackifier, at least one antioxidant, at least oneflame retardant, at least one filler, at least one plasticizer, at leastone processing aid, carbon black, at least one pigment, at least onebonding agent, at least one cure agent, at least one cure accelerator,at least one cure activator, or combinations thereof. The insulationcomposition may also further comprise one or more of cellulose fibers,sisal fibers, mineral wool fibers, nylon fibers, polyester fibers,polyimide fibers, polybenzimidazole fibers, polyaramid fibers, orcombinations thereof.

The present invention also relates to an insulation composition thatcomprises polybenzimidazole (“PBI”) fibers, basalt fibers, and at leastone nanoclay. In one embodiment, the PBI fibers may be of a specificlength, such as approximately ¼ of an inch. The PBI fibers may bepresent in the insulation composition at a range from approximately 2 wt% to approximately 8 wt % of a total weight of the insulationcomposition. The basalt fibers may be present at a range of fromapproximately 1 wt % to approximately 6 wt % of the total weight of theinsulation composition. Nanoclay may be present at a range of fromapproximately 5 wt % to approximately 10 wt % of the total weight of theinsulation composition. The insulation composition may further compriseone or more additives, such as at least one reinforcing agent, at leastone tackifier, at least one antioxidant, at least one flame retardant,at least one filler, at least one plasticizer, at least one processingaid, at least one retarder, carbon black, at least one pigment, at leastone bonding agent, at least one cure agent, at least one cureaccelerator, at least one cure activator, or combinations thereof. Theinsulation composition may further comprise a matrix agent such as arubber or a polymer, for example, but not limited to, NBR. Theinsulation composition may also further comprise one or more ofcellulose fibers, sisal fibers, mineral wool fibers, nylon fibers,polyester fibers, polyimide fibers, polyaramid fibers, or combinationsthereof.

The present invention, in a currently preferred embodiment, comprisesPBI fibers, NBR, basalt fibers, and nanoclay. In such a currentlypreferred embodiment, the NBR is present at 49.84 wt %, the PBI fibersare ¼ inch long and present at 5.89 wt %, basalt fibers are present at3.62 wt %, and the nanoclay is closite 10A and is present at 7.7 wt %.The currently preferred embodiment further comprises a reinforcing agentin the form of Hi-Sil® 233 present at 8.52 wt %, a flame retardant inthe form of Firebrake® ZB present at 3.62 wt %, an antioxidant in theform of Agerite® Stalite S present at 1.09 wt %, a tackifier in the formof SP25 present at 6.34 wt %, a cure agent in the from of SCSD-70present at 1.81 wt %, a plasticizer in the form of DOP-DLC-A present at7.25 wt %, a filler in the form of carbon black present at 0.63 wt %, acure accelerator in the form of Altax® present at 0.36 wt %, a cureactivator in the form of zinc oxide present at 2.08 wt %, a cureactivator in the form of stearic acid present at 1.00 wt %, and aretarder in the form of Retarder SAFE present at 0.23 wt %.

The present invention, in another embodiment, also relates to a rocketmotor that comprises a case, an insulation applied to an inner surfaceof the case, and a solid propellant disposed in the case. The insulationmay be an insulation comprising at least one NBR, basalt fibers, and atleast one nanoclay. The at least one NBR, basalt fibers, and nanoclaymay be present in the insulation in the amounts described above. Theinsulation may further comprise the additives and fibers describedabove. The insulation may further be an insulation comprising PBIfibers, basalt fibers, and at least one nanoclay. The PBI fibers, basaltfibers, and nanoclay may be present in the insulation in the amountsdescribed above. The insulation may further comprise one or more of thematrix agents, additives, and fibers described above.

The present invention, in a further embodiment, also relates to a methodof insulating a rocket motor. The method comprises applying aninsulation that may comprise at least one NBR, basalt fibers, and ananoclay to an inner surface of a rocket motor case and curing theinsulation. The at least one NBR, basalt fibers, and nanoclay may bepresent in the insulation in the amounts described above. The insulationmay further comprise the additives and fibers described above. Theinsulation may further be an insulation that comprises PBI fibers,basalt fibers, and a nanoclay. The PBI fibers, basalt fibers, andnanoclay may be present in the insulation in the amounts describedabove. The insulation may further comprise one or more of the matrixagents, additives, and fibers described above.

BRIEF DESCRIPTION OF THE SEVERAL VIEWS OF THE DRAWINGS

While the specification concludes with claims particularly pointing outand distinctly claiming that which is regarded as the present invention,the advantages of this invention may be more readily ascertained fromthe following description of the invention when read in conjunction withthe accompany drawing in which:

FIG. 1A is a cross-sectional view of a rocket motor that includes theinsulation composition of the present invention and FIG. 1B is anenlarged view of a portion of the rocket motor encircled in FIG. 1A.

DETAILED DESCRIPTION OF THE INVENTION

An insulation composition that includes at least one NBR, basalt fibers,and at least one nanoclay is disclosed. Further disclosed is aninsulation composition that includes PBI fibers, basalt fibers, and atleast one nanoclay. The insulation compositions may be used asinsulation to protect a rocket motor during combustion of a propellant,or in association with another article or assembly that would benefitfrom protection from heat and gases. The insulation composition may haverheological, physical, mechanical, electrostatic, and ablativeproperties that are improved or at least comparable to the properties ofa conventional ASNBR composition. For instance, the insulationcomposition may have better rheological and mechanical properties thanthe ASNBR composition and physical, electrostatic, and ablativeproperties that are similar to those of the ASNBR composition. Since theinsulation composition of the present invention is free of asbestos,environmental and health risks associated with the insulationcomposition may be substantially reduced or eliminated.

NBR used in insulation compositions according to the present inventionmay be a nitrile rubber having an acrylonitrile content that ranges fromapproximately 26 wt % to approximately 35 wt %, such as fromapproximately 30 wt % to approximately 35 wt %. The acrylonitrilecontent refers to the percentage of bound acrylonitrile in the NBR.Mixtures of NBRs, each having an acrylonitrile content within theabove-mentioned range, may also be used. The NBR may be unhydrogenatedor hydrogenated. Examples of NBRs that may be used in the insulationcomposition include, but are not limited to, those sold under the Nipol®tradename, such as Nipol® 1042, Nipol® 1052, Nipol® 1052-30, Nipol®1312, or mixtures thereof. The Nipol® products are copolymers ofacrylonitrile and butadiene and are commercially available from ZeonChemicals (Louisville, Ky.). Nipol® 1042 has an acrylonitrile contentthat ranges from approximately 32 wt % to approximately 34 wt %, aMooney viscosity at 1 00° C. that ranges from approximately 75 toapproximately 90, and a specific gravity of 0.98. Nipol® 1052 has anacrylonitrile content that ranges from approximately 32 wt % toapproximately 34 wt %, a Mooney viscosity at 100° C. that ranges fromapproximately 45 to approximately 60, and a specific gravity of 0.98.Nipol® 1052-30 is a lower Mooney viscosity version of Nipol® 1052 andhas an acrylonitrile content that ranges from approximately 32 wt % toapproximately 34 wt %, a Mooney viscosity at 100° C. that ranges fromapproximately 25 to approximately 40, and a specific gravity of 0.98.Nipol® 1312 is a liquid NBR and has an acrylonitrile content that rangesfrom approximately 27 wt % to approximately 30 wt %, a Brookfieldviscosity at 50° C. that ranges from approximately 20,000 centipoise(“cps”) to approximately 30,000 cps, and a specific gravity of 0.96.NBRs that may be used in the insulation composition are available underother trade names including, but not limited to, the Krynac®, Baymond,Paracil, or Perbunan® tradenames.

The PBI fibers used in insulation compositions of the present inventionare known in the art. As previously mentioned, PBI is known in the artas polybenzimidazole. PBI fibers may have a length that ranges fromapproximately 1/16 to approximately 1 inch. In one embodiment, ¼ inchfibers are used. PBI fibers are commercially available from PBIperformance Products Inc.

Basalt fiber is a material made from extremely fine fibers of basalt.Basalt fibers may vary in diameter from approximately 5 μm toapproximately 25 μm. Preferably, the fibers used in the presentinvention are greater than 5 μm in diameter as this is far enough abovethe respiratory limit to make basalt fiber a suitable replacement forasbestos. Basalt fibers are available from commercial sources such asFiberand Corp., Albarrie Canada Ltd., and under the brand name Basaltexfrom the Magureel Group.

Nanoclays are typically clays from the smectite family. Smectites have aunique morphology, featuring one dimension in the nanometer range.Smectite refers to a family of non-metallic clays primarily composed ofhydrated sodium calcium aluminum silicate. Common names for smectiteinclude montmorillonite or sodium montmorillonite (“sodium bentonite” or“Wyoming bentonite”) and swelling bentonite (“Western bentonite”).Nanoclays are available from commercial sources such as Southern ClayProducts Inc., Reade Advanced Materials, or Nanocor.

The amount of the basalt fibers, nanoclay and/or NBR, PBI fibers, andoptional ingredients in the insulation composition may be adjusted toachieve desired Theological, physical, mechanical, electrostatic, andablative properties, such as a desired viscosity, density, scorchresistance, cure time, Shore A hardness, tensile elongation (parallel tofibers and perpendicular to fibers), tensile strength (parallel tofibers and perpendicular to fibers), surface resistivity, volumeresistivity, dielectric constant, or relaxation time. Further the lengthor diameter of the basalt fibers and PBI fibers may be adjusted toachieve desired properties as enumerated supra.

The basalt fibers may be present in the insulation composition in a rageof from approximately 1 wt % of a total weight of the insulationcomposition to approximately 6 wt % of the total weight of theinsulation composition. Nanoclay may be present in the insulationcomposition in a range of from approximately 5 wt % of a total weight ofthe insulation composition to approximately 10 wt % of the total weightof the insulation composition.

The NBR may be present in the insulation composition in a range of fromapproximately 45 wt % of a total weight of the insulation composition toapproximately 56 wt % of the total weight of the insulation composition.The PBI fibers may be present in the insulation composition in a rangeof from approximately 2 wt % of the total weight of the insulationcomposition to approximately 8 wt % of the total weight of theinsulation composition. PBI fibers may have a length that ranges fromapproximately 1/16 of an inch to approximately 1 inch. It is currentlypreferred that ¼ inch PBI fibers are used.

The insulation composition may include at least one matrix agent.Suitable matrix agents include, but are not limited to, one or moreorganic elastomeric polymers. As referred to herein, the term. “organicelastomeric polymer” means a polymer having a backbone including carbonas a main component and free of metals or metalloids in the backbone.Generally, an elastomeric polymer is stretchable and compressible undermoderate tension with a relatively high tensile strength and memory sothat, upon release of the tension or compression, the elastomer retractstowards its original dimensions. Organic elastomers suitable for thepresent invention include ethylene propylene-diene monomer (EPDM)rubbers, natural rubber, butadiene-styrene copolymer rubbers, nitrilerubbers (such as NBR), polybutadiene rubbers, polyisoprene rubbers, andthe like.

Various mixtures, combinations, copolymers, and blends of theseexemplary rubbers are also included within the scope of the invention.

Suitable solid EPDM terpolymers having a 1,4-hexadiene component for usein this invention include NORDEL® 1040, NORDEL® 2522, and NORDEL® 2722E,made by DuPont Dow Elastomers of Wilmington, Del. Suitable solid EPDMterpolymers having an ENB diene component for use in this inventioninclude, without limitation, and as stated above, KELTAN® 4506, KELTAN®1446A, KELTAN® 2308, each of which is available from DSM Elastomers ofthe Netherlands, and NORDEL® IP 4520 and NORDEL® IP 4640, both of whichare and continue to be available from DuPont Dow Elastomers.

Small amounts of conventional fibers may optionally be present in theinsulation composition. These fibers may include, but are not limitedto, cellulose fibers, sisal fibers, mineral wool fibers, nylon fibers,polyester fibers, polyimide fibers, polybenzimidazole fibers, polyaramidfibers, or mixtures thereof.

The insulation composition may optionally include at least one additivefrom at least one of the following categories: a reinforcing agent, atackifier, an antioxidant, a flame retardant, a filler, a plasticizer, aprocessing aid, carbon black, a pigment, or a bonding agent to achievethe desired properties in the insulation composition. A specificingredient used in the insulation composition may provide one or morefunctions. One example of a reinforcing agent includes, but is notlimited to, Hi-Sil® 233. One example of a tackifying agent includes, butis not limited to, Picco™ 6100, which is an aromatic hydrocarbon resinavailable from Eastman Chemical Co. (Kingsport, Tenn.). Another exampleof a tackifying agent includes, but is not limited to, Akrochem® P-87,which is a phenolic resin that is available from Akrochem Chemical Corp.(Akron, Ohio). An antioxidant that may be used in the insulationcomposition includes, but is not limited to, Agerite® Stalite S, whichis available from R.T. Vanderbilt Chemical Company (Norwalk, Conn.).Organic or inorganic flame retardants that may be used include, but arenot limited to, Hi-Sil® 233 (amorphous, precipitated silica), Firebrake®ZB (zinc borate), Phos-Chek® P-30 (ammonium polyphosphate), Vertex® 60(magnesium hydroxide), Melapur® (a melamine derivative), talc, clay, ormixtures thereof. Hi-Sil® 233 is available from PPG Industries, Inc.(Pittsburgh, Pa.), Phos-Chek® P-30 is available from Monsanto (St.Louis, Mo.), Firebrake® ZB is available from US Borax Co. (Los Angeles,Calif.), Vertex® 60 is available from J.M. Huber Corp. (Edison, N.J.),and Melapur® is available from Ciba Specialty Chemicals Holding, Inc.(Basel, Switzerland). Mixtures of organic and inorganic flame retardantsmay also be used in the insulation composition.

Examples of fillers that may be used include, but are not limited to,silica, Vertex® 60, Oxyvinyls® 500F (polyvinyl chloride), which isavailable from OxyVinyls, LP (Dallas, Tex.), Mistron Vapor® (talc),which is available from Cyprus Mines Corp. (Englewood, Colo.), PolyplateHMT (delaminated kaolin clay), which is available from J.M. Huber Corp.(Edison, N.J.), or carbon black. An example of a plasticizer for NBRincludes, but is not limited to, dioctyl phthalate, which may beabsorbed on silica. As used herein, the term “DOP-DLC-A” refers todioctyl phthalate absorbed on silica. One example of a processing aidincludes, but is not limited to, stearic acid. In addition to thematerials described above, materials that provide similar functions orproperties to the insulation composition and that are sold underdifferent tradenames may also be used.

The insulation composition may also include a cure package, whichincludes a cure agent and, optionally, a cure accelerator, a cureactivator, a retarder, or combinations thereof. The cure agent may be asulfur cure agent, a peroxide cure agent, or a bromomethyl alkylatedphenolic resin. Examples of sulfur cure agents include, but are notlimited to, Crystex® OT-20 (an oil-treated polymeric sulfur), which isavailable from Flexsys America LP (Akron, Ohio), Akrosperse® IS-70 (a70% sulfur dispersion), which is available from Akrochem Chemical Corp.(Akron, Ohio), or other forms of elemental sulfur. Sulfur may also bedispersed in a rubber at approximately 70% concentration, such as aSCSD-70 polydispersion, which is a dispersion of 70% insoluble orpolymeric sulfur (Crystex®) in 30% of a SBR elastomeric binder. Examplesof peroxide cure agents include, but are not limited to, dicumylperoxide, 2,5-dimethyl-2,5-bis-(t-butylperoxy)hexane,2,5-dimethyl-2,5-bis-(benzoyl-peroxy)hexane,2,5-dimethyl-2,5-di(t-butylperoxy)-3-hexane,n-butyl-4,4-bis-(t-butylperoxyl)valerate,4,4′-methyl-bis-(cyclohexyl-amine)carbomate,1,1-bis-(t-butylperoxy)-3,3,5-trimethylcyclohexane,α,α′-bis-(t-butylperoxy)-diisopropylbenzene,2,5-dimethyl-2,5-bis-(t-butylperoxy)hexyne-3, t-butyl perbenzoate, ormixtures thereof. The cure agent may be present in the insulationcomposition from approximately 0.5 parts per hundred (“phr”) toapproximately 8 phr, such as from approximately 1.5 phr to approximately5 phr. As used herein, the term “phr” refers to parts by weight per onehundred parts by weight of the NBR.

The cure accelerator may be a phosphate cure accelerator, a butyl zimatematerial, a tetramethylthiuram monosulfide material, or a benzothiazyldisulfide material. Tetramethyl-thiuram monosulfide is available asAkrochem® TMTM from Akrochem Chemical Corp. (Akron, Ohio).Tetramethylthiuram monosulfide is also available under the Thionextradename. Benzothiazyl disulfide is sold under the Altax® tradename andis available from R.T. Vanderbilt Co., Inc. (Norwalk, Conn.). The cureactivator may be stearic acid or a metal oxide, such as zinc oxide ormagnesium oxide. Zinc oxide is available under the Kadox® tradename fromZinc Corp. of America (Monaca, Pa.), such as Kadox® 920C. In oneembodiment, the cure accelerator is Altax®, Akrochem® TMTM, or mixturesthereof and the cure activator is stearic acid, zinc oxide, orcombinations thereof. A retarder may be any agent used to reduce thescorching of rubber compounds at processing. In one embodiment theretarder is Retarder SAFE and is available from Akrochem Corp (Akron,Ohio).

The insulation composition may be prepared by mixing the basalt fibers,nanoclay with NBR and/or PBI fibers, and any optional ingredients thatmay be present to form a master batch. During mixing, the master batchmay reach a maximum temperature that ranges from approximately 290° F.to approximately 310° F. The master batch may be mixed until the basaltfibers, nanoclay, and any optional ingredients are substantially evenlydistributed in the matrix agent. For instance, the master batch may bemixed for an optimum amount of time to prevent damage to the basaltfibers or to the conventional fibers (if present). The temperature ofthe master batch may be lowered before adding the cure package toprevent premature curing of the insulation composition. For instance,during the curative mixing, the master batch may be exposed to a maximumtemperature that ranges from approximately 200° F. to approximately 220°F. before adding the cure package. The master batch and the cure packagemay be mixed until the insulation composition has a desired, rubber-likeconsistency. The insulation composition may be prepared in conventionalrubber mixing equipment, such as in an internal mixer, a sigma blademixer, a vertical blade mixer, or a compounding extruder mixer. Rubbermixing equipment is known in the art and, therefore, is not described indetail herein.

The insulation composition may be calendered or formed into a thinsheet, as known in the art, for use as insulation in a rocket motor. Anembodiment of a rocket motor 2 that utilizes the insulation compositionof the present invention as insulation 4 is shown in FIGS. 1A and 1B.FIG. 1B is an enlargement of the indicated portion of the rocket motor2. The insulation 4 may be applied to an interior surface of a case 6 ofthe rocket motor 2 by conventional techniques, such as by bonding theinsulation 4 to the case 6. The case 6 may be formed from a rigidmaterial, such as a metal, a composite material, or a combination of ametal and a composite material. The rocket motor 2 may also include asolid propellant 8, which is illustrated in FIGS. 1A and 1B as a centerperforation propellant. However, the invention is not limited to such.The solid propellant 8 may be an end-burning propellant or have anyother propellant configuration known in the art. The solid propellant 8may be disposed in the case 6. The solid propellant 8 may be aconventional propellant that is formulated to combust and produce thrustfor attaining rocket motor propulsion. A liner 10 may, optionally, beinterposed between the insulation 4 and the solid propellant 8.Compositions for the liner 10 and methods of applying the liner 10 tothe rocket motor 2 are known in the art and, therefore, are notdiscussed in detail herein. The insulation 4 and the liner 10, ifpresent, protect the case 6 of the rocket motor 2 from the extremetemperature and pressure conditions produced when the solid propellant 8is combusted.

The insulation 4 may be applied to the inner surface of the case 6 ofthe rocket motor 2 in an uncured form and then cured. For instance, asheet of the insulation 4 may be laid up or cast into the rocket motor 2and cured. An adhesive layer (not shown) may, optionally, be used tobond the insulation 4 to the inner surface of the case 6 of the rocketmotor 2. Adhesive layers are known in the art and, therefore,compositions of adhesive layers and application of the adhesive layer isnot discussed in detail herein. However, for the sake of example only,Chemlok® adhesives may be used to bond the insulation 4 to the innersurface of the case 6 of the rocket motor 2. The insulation 4 may alsobe applied in an uncured form to a mandrel, cured, and subsequent layersof the rocket motor 2 formed over the insulation 4. Alternatively, theinsulation 4 may be cured, cut into appropriate sizes or geometries, andapplied to the inner surface of the rocket motor 2 using an adhesivelayer. For the sake of example only, the insulation 4 may be cured forfrom approximately 60 minutes to approximately 120 minutes at atemperature that ranges from approximately 290° F. to approximately 300°F. and at a pressure of between approximately 50 psi and approximately200 psi. However, additional temperatures, pressures, or amounts of timemay be used to cure the insulation 4. For instance, lower or highertemperatures may be used if the cure time is adjusted accordingly. Thecured insulation 4 may form a reduced bond line with the surface of therocket motor 2.

Upon combustion of the solid propellant 8, combustion products of thesolid propellant 8 may be directed into nozzle 12 and expelled,producing thrust to propel the rocket motor 2. A char may form on theinsulation 4 as flames produced by the combusting solid propellant 8contact the insulation 4. While the insulation 4 is ablative and isultimately consumed during combustion of the solid propellant 8, thechar may remain on the insulation 4 for an amount of time sufficient toprotect the rocket motor 2. The char is a good insulator and may protectthe insulation 4 from ablating at an undesirably fast rate by remainingattached to the insulation 4 for a longer period of time. As such, therocket motor 2 may be protected from the extreme temperature andpressure conditions produced by combustion of the solid propellant 8.

The insulation compositions of the present invention may be formulatedas a drop-in replacement for a conventional ASNBR composition.Therefore, the insulation compositions may be used in existing rocketmotors without needing to significantly adjust the processing andloading techniques currently used to prepare and load the ASNBRcomposition.

In addition to being used as insulation in a rocket motor, theinsulation compositions of the present invention may be used in otherarticles where protection from heat and gases is desired. For example,the insulation compositions may be used for heat and gas protection inunder-the-hood applications in automobiles. The insulation compositionsmay also be used in conveyor belts, noise damping applications inautomobile and other fields, or in other routine rubber applications,such as hoses, gaskets, seals, isolators and mounts, cushions, airemission hoses, or dock fenders.

The following examples serve to explain certain non-limiting embodimentsof the insulation compositions of the present invention in more detail.These examples are not to be construed as being exhaustive or exclusiveas to the scope of the invention.

EXAMPLES Example 1 Formulations of Insulation Compositions

Insulation compositions having the ingredients shown in Table 1 wereformulated by mixing all of the ingredients, except for the curepackage, to form a master batch. During mixing, the temperature of themaster batch was maintained at less than or equal to approximately 310°F. The ingredients of the master batch were mixed for up toapproximately 25 minutes. The temperature of the master batch wasreduced to less than or equal to approximately 220° F. before adding theingredients of the cure package, which were mixed in with the masterbatch for up to approximately 5 minutes. The resulting insulationcompositions had a rubber-like consistency. TABLE 1 InsulationCompositions having an NBR(s) and PBI Fibers and/or Nanoclay. RDL6098RDL6099 RDL7000 RDL7023 RDL7068 RDL7069 RDL7083 RDL7094 Ingredient (wt%) (wt %) (wt %) (wt %) (wt %) (wt %) (wt %) (wt %) Nipol ® 1052 26 2626 23.38 22.85 18.12 18.24 18.24 Nipol ® 1042 26 26 26 23.38 22.85 27.1927.36 24.62 Nipol ® 1312 — — — 4.97 4.57 4.53 4.56 7.3 Stearic acid 1.011.01 1.01 1.00 1.01 1.00 1.00 1.00 Picco ® 6100 3.89 3.89 3.89 3.87 — —— — SP25 — — — — 6.4 6.34 6.38 6.38 Agerite ® Stalite S 1.05 1.05 1.051.04 1.10 1.09 1.09 1.09 Hi-Sil ® 233 8.83 8.83 8.83 8.78 8.59 8.52 8.578.57 Polyplate HMT — — — — 7.77 — — — Cloisite 10A Nanoclay 8.00 8.008.00 7.96 — 7.70 7.75 7.75 Basalt Fibers 3.78 — — 3.76 3.66 3.62 3.653.65 Firebrake ® ZB 3.7 3.7 3.7 3.68 3.66 3.62 3.65 3.65 PBI Fibers (¼″long) 6.00 6.00 3.78 5.97 5.94 5.89 5.93 5.93 DOP-DLC-A 8.00 8.00 8.007.96 7.31 7.25 7.30 7.30 Naugex MBTS — — — — — — 0.36 0.36 Carbon black— — — — — 0.63 — — Zinc oxide 2.12 2.12 2.12 2.11 2.10 2.08 2.10 2.10Altax ® 0.38 0.38 0.38 0.38 0.37 0.36 — — Crystex ® Sulfur 1.24 1.241.24 — — — — — SCSD-70 Polydispersion — — — 1.76 1.83 1.81 1.82 1.82P-84¹ — 3.78 6.00 — — — — — Retarder SAFE — — — — — 0.23 0.23 0.23¹Polyimide fibers available from Lenzing AG (Lenzing, Austria)

Example 2 Rheological Properties of the Insulation Compositions

The rheological properties of the insulation compositions described inExample 1 were determined by conventional techniques. The results of therheological testing are shown in Table 2. For comparative purposes, therheological properties of an ASNBR composition are also provided. TheASNBR composition is produced by Esterline-Kirkhill Elastomers. TABLE 2Rheological Properties of ASNBR, RDL6098, RDL6099, RDL7000, RDL7023,RDL7069, RDL7083, and RDL7094. Property ASNBR RDL6098 RDL6099 RDL7000RDL7023 RDL7069 RDL7083 RDL7094 Mooney 44-88 61.22 62.06 68.71 42.6340.17 41.48 34.63 Viscosity¹ (MV) Mooney Scorch²  5-30 8.39 7.66 8.158.99 10.51 11.5 12.49 (minutes) TC90 64.73 39.26 36.25 35.21 38.1 34.2735.03 37.23 (minutes)³¹MU at 212° F.²MS + 1 at 290° F. (as determined by ASTM D 1646)³TC90 is the 90 percent cure time measured by ODR at 300° F. (asdetermined by ASTM D2084)

As shown in Table 2, the insulation compositions had similar or improvedrheological properties compared to the properties of the ASNBRcomposition.

Example 3 Physical, Mechanical, and Electrostatic Properties of theInsulation Compositions

Physical, mechanical, and electrostatic properties of the insulationcompositions described in Example 1 are shown in Table 3. Theseproperties were determined by conventional techniques. The values forthe mechanical properties of RDL7069 were measured at 2″/minute, whilethose for RDL6098, RDL6099, RDL7000, RDL7023, RDL7083, and RDL7094, andASNBR were measured at 20″/minute. For comparative purposes, thephysical, mechanical, and electrostatic properties of the ASNBRcomposition are also shown. TABLE 3 Physical, Mechanical, andElectrostatic Properties of ASNBR, RDL6098, RDL6099, RDL7000, RDL7023,RDL7069, RDL7083, and RDL7094. Property ASNBR RDL6098 RDL6099 RDL7000RDL7023 RDL7069 RDL7083 RDL7094 Density (g/cm³)¹ 1.255-1.305 1.20141.1809 1.1787 1.1943 1.1833 1.19 1.19 Shore A Hardness² 75-85 76.4 79.481.5 69.6 71.2 71.9 71.4 Tensile Elongation 50+ 488 153 107 485 576 482468 parallel to fibers) (%)³ Tensile Elongation 225+ 517 368 420 498 568461 529 (perpendic. to fibers) (%)³ Tensile Strength 1000+ 1230 11101210 969 914 947 713 (parallel to fibers) (%)³ Tensile Strength 700+1010 831 811 777 746 696 674 (perpendic. to fibers) (%)³ SurfaceResistivity 6.1 × 10¹² 7.04 × 10¹¹ 7.48 × 10¹¹ 11.12 × 10¹¹ 5.67 × 10¹¹7.68 × 10¹¹ 1.48 × 10¹² 9.86 × 10¹¹ (ohms/sq) Volume Resistivity 6.6 ×10¹² 3.31 × 10¹¹ 4.20 × 10¹¹  4.22 × 10¹¹ 9.18 × 10¹⁰ 1.72 × 10¹¹ 3.90 ×10¹¹ 3.46 × 10¹¹ (ohm-cm) Dielectric constant 8.75 7.08 6.71 6.05 7.457.19 6.35 6.75 Relaxation time (sec) 5.10 0.21 0.25 0.22 0.06 0.11 0.220.20¹As determined by ASTM D792²As determined by ASTM D2240³As determined by ASTM D412

The insulation compositions of the present invention had physical,mechanical, and electrostatic properties similar to the desirableproperties of the ASNBR composition. The insulation compositions had aslightly lower density than that of the ASNBR composition. Tensileproperties of the insulation compositions were exceptional and greatlyimproved over that of the ASNBR composition or other synthetic fiberfilled formulations. The other properties of the insulation compositionswere similar to those of the ASNBR composition.

Example 4 Ablative Performance of the Insulation Compositions

The ablative performance of the insulation compositions described inExample 1 was determined in a high mach seventy pound char motor. Eachof the insulation compositions was formed into a thin sheet and testedin the char motor. As known in the art, the char motor simulated typicaltemperature and pressure conditions in a low velocity, mid velocity, orhigh velocity section of a conventional rocket motor. The thickness ofeach of the insulation compositions was measured at selected intervals,nominally one inch apart, before firing the char motor. The weight ofeach of the insulation compositions was also measured before firing. Theinsulation compositions were then assembled into the low velocitysection, the middle velocity section, and the high velocity section ofthe char motor. After firing, the char motor was disassembled, and thethickness and weight of each insulation composition was measured again.The rate at which the insulation composition is reduced or erodes isexpressed in terms of the reduction of the thickness of the insulationcomposition per second and is referred to as the material affected rateor material ablation rate (“MAR”). The MAR of the insulation compositionwas determined by subtracting the post-fired thickness of virgininsulation (i.e., after the char had been removed) at a given point fromthe pre-fired thickness at the same point and dividing the result by theburn time of the motor. The average weight loss of the insulationcomposition was determined as a function of the pre-fired weight. TheMAR and average weight loss are indicators of damage to the insulationcomposition (ablation), where lower numbers indicate better insulativeand ablative performance. The ablative performance of the insulationcompositions is shown in Table 4. TABLE 4 Ablative Performance forASNBR, RDL6098, RDL6099, RDL7000, RDL7023, RDL7069, RDL7083, andRDL7094. Property ASNBR RDL6098 RDL6099 RDL7000 RDL7023 RDL7069 RDL7083RDL7094 Motor # 1239 1251 1229 1229 1239 1251 1270 1270 Low velocityregion: 3.21 3.49 3.84 3.85 4.13 3.96 3.98 3.57 Average MAR (mils/sec)Low velocity region: 9.66 10.87 10.90 10.86 11.57 11.59 10.56 10.56Average Weight Loss (%) Mid velocity region: 9.62 8.86 10.18 8.92 9.298.07 9.5 9.27 Average MAR (mils/sec) Mid velocity region: 11.26 10.8711.76 10.97 11.80 11.97 10.84 10.32 Average Weight Loss (%) Highvelocity region: 15.02 13.45 11.55 14.89 14.31 12.98 13.19 14.39 AverageMAR (mils/sec) High velocity region: 15.78 15.60 16.92 17.78 15.92 15.7914.8 14.442 Average Weight Loss (%)

The results in Table 4 show that insulative compositions according tothe present invention have ablative properties that are similar to thoseof the ASNBR composition.

In summary, the insulation compositions of the present invention hadsimilar or better Theological properties and similar physical,electrostatic, and ablative properties compared to the ASNBRcomposition. Further the insulation compositions of the presentinvention had improved mechanical properties when compared to the ASNBRcomposition. As such, the insulation compositions are suitable drop-inreplacements for the ASNBR composition.

While the invention may be susceptible to various modifications andalternative forms, specific embodiments have been shown by way ofexample in the drawings and have been described in detail herein.However, it should be understood that the invention is not intended tobe limited to the particular forms disclosed. Rather, the invention isto cover all modifications, equivalents, and alternatives falling withinthe spirit and scope of the invention as defined by the followingappended claims.

1. An insulation composition comprising: at least one of a nitrilebutadiene rubber and polybenzimidazole fibers; basalt fibers; andnanoclay.
 2. The insulation composition of claim 1, wherein thecomposition comprises a nitrile butadiene rubber.
 3. The insulationcomposition of claim 2, wherein the at least one nitrile butadienerubber comprises a copolymer of acrylonitrile and butadiene.
 4. Theinsulation composition of claim 2, wherein the nitrile butadiene rubbercomprises from approximately 35% by weight to approximately 56% byweight of a total weight of the insulation composition.
 5. Theinsulation composition of claim 1, wherein the basalt fibers comprisefrom approximately 1% by weight to approximately 6% by weight of a totalweight of the insulation composition.
 6. The insulation composition ofclaim 1, wherein the basalt fibers have a diameter that is at least 5μm.
 7. The insulation composition of claim 1, wherein the basalt fibershave a diameter that ranges from approximately 5 μm to approximately 25μm.
 8. The insulation composition of claim 1, wherein the nanoclaycomprises from approximately 5% by weight to approximately 10% by weightof a total weight of the insulation composition.
 9. The insulationcomposition of claim 1, wherein the nanoclay is Closite 10A.
 10. Theinsulation composition of claim 1, further comprising one or more of atleast one reinforcing agent, at least one tackifier, at least oneantioxidant, at least one flame retardant, at least one filler, at leastone plasticizer, at least one processing aid, at least one retarder,carbon black, at least one pigment, at least one bonding agent, at leastone cure agent, at least one cure accelerator, at least one cureactivator, or combinations thereof.
 11. The insulation composition ofclaim 1, further comprising one or more of cellulose fibers, sisalfibers, mineral wool fibers, nylon fibers, polyester fibers, polyimidefibers, polybenzimidazole fibers, polyaramid fibers, combinations andmixtures thereof.
 12. The insulation composition of claim 1, wherein thecomposition comprises polybenzimidazole fibers.
 13. The insulationcomposition of claim 12, wherein the polybenzimidazole fibers comprisefrom approximately 2% by weight to approximately 8% by weight of a totalweight of the insulation composition.
 14. The insulation composition ofclaim 12, wherein the polybenzimidazole fibers have a length that rangesfrom approximately 1/16 of an inch to approximately 1 inch.
 15. Theinsulation composition of claim 12, wherein the polybenzimidazole fibershave a length of approximately ¼ of an inch.
 16. The insulationcomposition of claim 1, further comprising at least one matrix agent.17. The insulation composition of claim 16, wherein the at least onematrix agent is selected from the group consisting of ethylenepropylene-diene monomer rubbers, natural rubbers, butadiene-styrenecopolymer rubbers, nitrile rubbers, polybutadiene rubbers, andpolyisoprene rubbers.
 18. The insulation composition of claim 1, whereinthe composition comprises polybenzimidazole fibers and a nitrilebutadiene rubber.
 19. The insulation composition of claim 18, whereinthe at least one nitrile butadiene rubber comprises from approximately35% by weight to approximately 56% by weight of a total weight of theinsulation composition.
 20. The insulation composition of claim 18,wherein the basalt fibers comprise from approximately 1% by weight toapproximately 6% by weight of a total weight of the insulationcomposition.
 21. The insulation composition of claim 18, wherein thebasalt fibers have a diameter that is at least 5 μm.
 22. The insulationcomposition of claim 18, wherein the basalt fibers have a diameter thatranges from approximately 5 μm to approximately 25 μm.
 23. Theinsulation composition of claim 18, wherein the nanoclay comprises fromapproximately 5% by weight to approximately 10% by weight of a totalweight of the insulation composition.
 24. The insulation composition ofclaim 18, wherein the nanoclay is Closite 10A.
 25. The insulationcomposition of claim 18, further comprising one or more of at least onereinforcing agent, at least one tackifier, at least one antioxidant, atleast one flame retardant, at least one filler, at least oneplasticizer, at least one processing aid, at least one retarder, carbonblack, at least one pigment, at least one bonding agent, at least onecure agent, at least one cure accelerator, at least one cure activator,or combinations thereof.
 26. The insulation composition of claim 18,further comprising one or more of cellulose fibers, sisal fibers,mineral wool fibers, nylon fibers, polyester fibers, polyimide fibers,polyaramid fibers, combinations and mixtures thereof.
 27. The insulationcomposition of claim 18, wherein the polybenzimidazole fibers comprisefrom approximately 2% by weight to approximately 8% by weight of a totalweight of the insulation composition.
 28. The insulation composition ofclaim 18, wherein the polybenzimidazole fibers have a length that rangesfrom approximately 1/16 of an inch to approximately 1 inch.
 29. Theinsulation composition of claim 12, wherein the polybenzimidazole fibershave a length of approximately ¼ of an inch.
 30. The insulationcomposition of claim 18, further comprising at least one matrix agent.31. The insulation composition of claim 30, wherein the at least onematrix agent is selected from the group consisting of ethylenepropylene-diene monomer rubbers, natural rubbers, butadiene-styrenecopolymer rubbers, nitrile rubbers, polybutadiene rubbers, andpolyisoprene rubbers.
 32. A rocket motor, comprising: a case, aninsulation applied to an inner surface of the case and a solidpropellant disposed in the case, wherein the insulation comprises: atleast one of a nitrile butadiene rubber and polybenzimidazole fibers;basalt fibers; and nanoclay.
 33. The rocket motor of claim 32, whereinthe insulation comprises a nitrile butadiene rubber.
 34. The rocketmotor of claim 33, wherein the at least one nitrile butadiene rubbercomprises a copolymer of acrylonitrile and butadiene.
 35. The rocketmotor of claim 33, wherein the nitrile butadiene rubber comprises fromapproximately 35% by weight to approximately 56% by weight of a totalweight of the insulation composition.
 36. The rocket motor of claim 32,wherein the basalt fibers comprise from approximately 1% by weight toapproximately 6% by weight of a total weight of the insulationcomposition.
 37. The rocket motor of claim 32, wherein the basalt fibershave a diameter that is at least 5 μm.
 38. The rocket motor of claim 32,wherein the basalt fibers have a diameter that ranges from approximately5 μm to approximately 25 μm.
 39. The rocket motor of claim 32, whereinthe nanoclay comprises from approximately 5% by weight to approximately10% by weight of a total weight of the insulation composition.
 40. Therocket motor of claim 32, wherein the nanoclay is Closite 10A.
 41. Therocket motor of claim 32, further comprising one or more of at least onereinforcing agent, at least one tackifier, at least one antioxidant, atleast one flame retardant, at least one filler, at least oneplasticizer, at least one processing aid, at least one retarder, carbonblack, at least one pigment, at least one bonding agent, at least onecure agents at least one cure accelerator, at least one cure activator,or combinations thereof.
 42. The rocket motor of claim 32, furthercomprising one or more of cellulose fibers, sisal fibers, mineral woolfibers, nylon fibers, polyester fibers, polyimide fibers,polybenzimidazole fibers, polyaramid fibers, or combinations thereof.43. The rocket motor of claim 32, wherein the insulation comprisespolybenzimidazole fibers.
 44. The rocket motor of claim 43, wherein thepolybenzimidazole fibers comprise from approximately 2% by weight toapproximately 8% by weight of a total weight of the insulationcomposition.
 45. The rocket motor of claim 43, wherein thepolybenzimidazole fibers have a length that ranges from approximately1/16 of an inch to approximately 1 inch.
 46. The rocket motor of claim43, wherein the polybenzimidazole fibers have a length of approximately¼ of an inch.
 47. The rocket motor of claim 32, further comprising atleast one matrix agent.
 48. The rocket motor of claim 47, wherein the atleast one matrix agent is selected from the group consisting of ethylenepropylene-diene monomer rubbers, natural rubbers, butadiene-styrenecopolymer rubbers, nitrile rubbers, polybutadiene rubbers, andpolyisoprene rubbers.
 49. The rocket motor of claim 32, wherein therocket motor comprises polybenzimidazole fibers and a nitrile butadienerubber.
 50. A method of insulating a rocket motor, comprising: applyingan insulation that comprises basalt fibers, nanoclay, and at least oneof a nitrile butadiene rubber and polybenzimidazole fibers to an innersurface of a rocket motor case; and curing the insulation.
 51. Themethod of claim 50, wherein applying an insulation that comprises basaltfibers, nanoclay, and at least one of a nitrite butadiene rubber andpolybenzimidazole fibers to an inner surface of a rocket motor casecomprises applying an insulation that comprises from approximately 35%by weight to approximately 56% by weight of nitrite butadiene rubber tothe inner surface of the rocket motor case.
 52. The method of claim 50,wherein applying an insulation that comprises basalt fibers, nanoclay,and at least one of a nitrite butadiene rubber and polybenzimidazolefibers to an inner surface of a rocket motor case comprises applying aninsulation that comprises from approximately 5% by weight toapproximately 10% by weight of nanoclay to the inner surface of therocket motor case.
 53. The method of claim 50, wherein applying aninsulation that comprises basalt fibers, nanoclay, and at least one of anitrite butadiene rubber and polybenzimidazole fibers to an innersurface of a rocket motor case comprises applying an insulation thatcomprises from approximately 1% by weight to approximately 6% by weightof basalt fibers to the inner surface of the rocket motor case.
 54. Themethod of claim 50, wherein applying an insulation that comprises basaltfibers, nanoclay, and at least one of a nitrite butadiene rubber andpolybenzimidazole fibers to an inner surface of a rocket motor casecomprises applying an insulation that comprises from approximately 2% byweight to approximately 8% by weight of polybenzimidazole fibers to theinner surface of the rocket motor case.